Dynaflow® melts and flows at temperatures very close to Stay-Silv® 15 and provides comparable brazed mechanical properties. This makes Dynaflow® an excellent cost-effective alternative to the 15% silver alloys. This premium, medium range silver alloy has been meticulously formulated to even tighter specifications than our standard copper-to-copper alloys.
Features
• Premium, medium-range, alloy for brazing copper or brass.
• Excellent strength and ductility.
• Economical replacement of 15% silver alloys.
• When heated above its liquidus, can penetrate tight connections.
• Wide melting range provides ability to fill loose connections and "cap" or "build-up" around the finished joint.
• Self-fluxing on copper and copper-to-copper connections. Use Stay-Silv® white flux for brazing brass or copper-to brass.
• Corrosion resistance is generally similar to the copper base metal
• Not recommended for brazing steel or other ferrous base metals
• Due to its phosphorus content, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
• Complies with the EU Reach & RoHS directive
Typical Applications
• Copper-to-copper brazing
Features
• Premium, medium-range, alloy for brazing copper or brass.
• Excellent strength and ductility.
• Economical replacement of 15% silver alloys.
• When heated above its liquidus, can penetrate tight connections.
• Wide melting range provides ability to fill loose connections and "cap" or "build-up" around the finished joint.
• Self-fluxing on copper and copper-to-copper connections. Use Stay-Silv® white flux for brazing brass or copper-to brass.
• Corrosion resistance is generally similar to the copper base metal
• Not recommended for brazing steel or other ferrous base metals
• Due to its phosphorus content, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
• Complies with the EU Reach & RoHS directive
Typical Applications
• Copper-to-copper brazing